High Carbon Artificial Graphite Petro Coke for Foundry

Transport Package
Mt Bag or 25kg Bag Into Mt Bag
Specification
1-5mm/0.2-1
Trademark
HQ
Origin
Inner Mongolia
HS Code
3801100090
Production Capacity
120, 000tons Per Year
Reference Price
$ 540.00 - 792.00
Contact Us

Product Description

                       High Carbon Artificial Graphite Petro Coke  for Foundry 

Specifications
Type Fixed Carbon
Min 		Sulphur
Max
  		Moisture 
Max 		Ash
Max
  		Volatile 
Max 		N itrogen
Max 		Size(mm)
GPC-01 99% 0.03% 0.5% 0.5% 0.5% 0.01% 1-5mm
GPC-02 99% 0.05% 0.5% 0.5% 0.5% 0.03% 1-5mm
GPC-03 98.5% 0.07% 0.5% 0.5% 0.7% 0.03% 0.2-1mm
GPC-04 98.5% 0.1% 0.5% 0.5% 0.7% 0.03% 0-0.2mm
Any other sizes can also be produced as customer's requirements

Graphite petroleum coke (GPC)
High quality green coke is taken into Acheson furnace for graphitization process with temperature around 2500-3600 ºC, lower Nitrogen content below 300ppm, accordingly sulphur, water, ash content all reduced, to ensure carbon content at above 98%, widely used in iron and steel casting industry to lower production cost and reduce raw material waste.
High Carbon Artificial Graphite Petro Coke for Foundry

Our company
We are the leading manufacturer of carbon additives in China  for 10 years , mainly produce g raphite petroleum coke, calcined petroleum coke, pet coke  and  silicon carbide , meanwhile we can trade metallurgical coke and foundry coke as your requirement.   The products are widely used in metallurgy, chemical industry, steel-making, casting industry and many fields.

Our factory
H av ing  5 own factories located in Lanzhou Gansu, Linyi Shandong, Ulanchabu Inner Mongolia, Hami Xinjiang and Binhai Tian jing with 8 big electric resistance furnaces, we can supply sufficient Graphite petroleum coke annual production in 80,000 tons, Semi Graphite petroleum coke annual production 40,000 tons and calcined petroleum coke annual production in 150,000 tons. Special particle size is available for your requirements.


 

 

Graphite & Products

SUPERAUTO.CAT, 2023